- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ASTM D 792 | ||
| Thickness | 25.0 microns | 0.984 mil | |||
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D 1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 11.0 MPa | 1600 psi | ASTM D 882 | ||
| Film Tensile Strength at Yield, TD | 11.0 MPa | 1600 psi | ASTM D 882 | ||
| Film Elongation at Break, MD | 540 % | 540 % | ASTM D 882 | ||
| Film Elongation at Break, TD | 830 % | 830 % | ASTM D 882 | ||
| Elmendorf Tear Strength MD | 100 g | 100 g | ASTM D 1922 | ||
| Elmendorf Tear Strength TD | 330 g | 330 g | ASTM D 1922 | ||
| Elmendorf Tear Strength, MD | 4.00 g/micron | 102 g/mil | ASTM D 1922 | ||
| Elmendorf Tear Strength, TD | 13.2 g/micron | 335 g/mil | ASTM D 1922 | ||
| Dart Drop | 4.00 g/micron | 102 g/mil | F50; ASTM D 1709/A | ||
| Dart drop Test | 100 g | 0.221 lb | F50; ASTM D 1709/A | ||
| Film Tensile Strength at Break, MD | 49.0 MPa | 7110 psi | ASTM D 882 | ||
| Film Tensile Strength at Break, TD | 34.0 MPa | 4930 psi | ASTM D 882 | ||
| 1% Secant Modulus, MD | 200 MPa | 29000 psi | ASTM D 882 | ||
| 1% Secant Modulus, TD | 230 MPa | 33400 psi | ASTM D 882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 11 % | 11 % | ASTM D 1003 | ||
| Gloss | 56 % | 56 % | 45°; ASTM D 2457 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 195 - 220 °C | 383 - 428 °F | |||
| Die Opening | 0.0900 - 0.220 cm | 0.0354 - 0.0866 in | |||
| Blow-up Ratio (BUR) | 2.0 - 3.0 | 2.0 - 3.0 | Optimum | ||
| Descriptive Properties | |||||
| Low Friction Puncture | 34 (J/mm) | NOVA Chemicals test method | |||