- 熔体流动速率 [g/10min]: 5.9
- 密度 [g/cm3]: 0.919
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.919 g/cc | 0.0332 lb/in³ | ASTM D 792 | ||
| Thickness | 20.0 microns | 0.787 mil | |||
| Melt Flow | 5.9 g/10 min @Load 2.16 kg, Temperature 190 °C | 5.9 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D 1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 8.50 MPa | 1230 psi | ASTM D 882 | ||
| Film Tensile Strength at Yield, TD | 8.30 MPa | 1200 psi | ASTM D 882 | ||
| Film Elongation at Break, MD | 472 % | 472 % | ASTM D 882 | ||
| Film Elongation at Break, TD | 647 % | 647 % | ASTM D 882 | ||
| Elmendorf Tear Strength MD | 320 g | 320 g | ASTM D 1922 | ||
| Elmendorf Tear Strength TD | 520 g | 520 g | ASTM D 1922 | ||
| Elmendorf Tear Strength, MD | 16.0 g/micron | 406 g/mil | ASTM D 1922 | ||
| Elmendorf Tear Strength, TD | 26.0 g/micron | 660 g/mil | |||
| Dart drop Test | 131 g | 0.289 lb | 7; ASTM D 1709/A | ||
| Film Tensile Strength at Break, MD | 28.3 MPa | 4100 psi | ASTM D 882 | ||
| Film Tensile Strength at Break, TD | 22.2 MPa | 3220 psi | ASTM D 882 | ||
| 1% Secant Modulus, MD | 116 MPa | 16800 psi | ASTM D 882 | ||
| 1% Secant Modulus, TD | 135 MPa | 19600 psi | ASTM D 882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 1.0 % | 1.0 % | ASTM D 1003 | ||
| Gloss | 91.5 % | 91.5 % | at 45°; ASTM D 2457 | ||
| Descriptive Properties | |||||
| Low Friction Puncture (J/mm) | 52 | NOVA Chemicals Test Method | |||