- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.917
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in³ | ASTM D792 |
| Thickness | 25.0 microns | 0.984 mil | |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 9.03 MPa | 1310 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 9.03 MPa | 1310 psi | ASTM D882 |
| Film Elongation at Yield, MD | 550 % | 550 % | ASTM D638 |
| Film Elongation at Yield, TD | 725 % | 725 % | ASTM D882 |
| Puncture Energy | 1.75 J | 1.29 ft-lb | Low Friction Puncture |
| Elmendorf Tear Strength MD | 320 g | 320 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 480 g | 480 g | ASTM D1922 |
| Dart drop Test | 800 g | 1.76 lb | ASTM D1709/A |
| Film Tensile Strength at Break, MD | 43.0 MPa | 6240 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 34.0 MPa | 4930 psi | ASTM D882 |
| 1% Secant Modulus, MD | 134.96 MPa | 19575 psi | ASTM D882 |
| 1% Secant Modulus, TD | 144.96 MPa | 21025 psi | ASTM D882 |
| Heat Seal Strength Initiation Temperature | 100 °C | 212 °F | 2N |
| Optical Properties | Metric | English | Comments |
| Haze | 17 % | 17 % | ASTM D1003 |
| Gloss | 32 % | 32 % | at 45°; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 185 - 200 °C | 365 - 392 °F | |