- 熔体流动速率 [g/10min]: 19.0
- 密度 [g/cm3]: 0.925
- 拉伸强度 [MPa]: 10.0
- 弯曲模量 [MPa]: 0.345
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.925 g/cc | 0.0334 lb/in³ | ASTM D792 |
| Environmental Stress Crack Resistance | <= 10 hour | <= 10 hour | F50; Condition A, 100% Igepal; ASTM D1693 |
| Melt Flow | 19 g/10 min @Load 2.16 kg, Temperature 190 °C | 19 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 52 | 52 | ASTM D2240 |
| Tensile Strength, Yield | 10.0 MPa | 1450 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 850 % | 850 % | 50 mm/min; ASTM D 638 |
| Flexural Modulus | 0.345 GPa | 50.0 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 85.0 °C | 185 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 170 - 215 °C | 338 - 419 °F | |