- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ASTM D792 |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 8.00 MPa | 1160 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 8.00 MPa | 1160 psi | ASTM D882 |
| Film Elongation at Break, MD | 550 % | 550 % | ASTM D882 |
| Film Elongation at Break, TD | 840 % | 840 % | ASTM D882 |
| Secant Modulus, MD | 0.140 GPa | 20.3 ksi | at 1%; ASTM D882 |
| Secant Modulus, TD | 0.150 GPa | 21.8 ksi | at 1%; ASTM D882 |
| Impact | 185 | 185 | J/mm; NOVA Chemicals Puncture test |
| Elmendorf Tear Strength, MD | 16.0 g/micron | 406 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 30.0 g/micron | 762 g/mil | ASTM D1922 |
| Dart Drop | 8.00 g/micron | 203 g/mil | F50, ASTM D1709/A |
| Film Tensile Strength at Break, MD | 45.0 MPa | 6530 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 2.0 % | 2.0 % | ASTM D1003 |
| Gloss | 90 % | 90 % | at 45°; 1 mil; ASTM D2457 |