- 熔体流动速率 [g/10min]: 4.8
- 密度 [g/cm3]: 0.925
- 弯曲强度 [MPa]: 10.5
- 弯曲模量 [MPa]: 0.520
- 热变形温度 [℃]: 42.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.925 g/cc | 0.0334 lb/in³ | ASTM D792 |
| ESCR 100% Igepal® | >= 1000 hour @Temperature 50.0 °C | >= 1000 hour @Temperature 122 °F | F50; Condition A, From compression molded specimens; ASTM D1693 |
| ESCR 10% Igepal® | >= 1000 hour @Temperature 50.0 °C | >= 1000 hour @Temperature 122 °F | F50; Condition A, From compression molded specimens; ASTM D1693 |
| Melt Flow | 4.8 g/10 min @Load 2.16 kg, Temperature 190 °C | 4.8 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 10.5 MPa @Thickness 3.17 mm | 1520 psi @Thickness 0.125 in | Type IV specimen, 2" per minute test speed, rotomolded samples; ASTM D638 |
| Flexural Modulus | 0.520 GPa | 75.4 ksi | 1% Strain Value from rotomolded samples; ASTM D790 |
| Impact Test | 67.8 J @Thickness 3.17 mm, Temperature -40.0 °C | 50.0 ft-lb @Thickness 0.125 in, Temperature -40.0 °F | rotomolded; ARM Method |
| 203 J @Thickness 6.35 mm, Temperature -40.0 °C | 150 ft-lb @Thickness 0.250 in, Temperature -40.0 °F | rotomolded; ARM Method | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 42.0 °C | 108 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 35.0 °C | 95.0 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 170 - 215 °C | 338 - 419 °F | |