- 熔体流动速率 [g/10min]: 400.0
- 密度 [g/cm3]: 0.9115
- 弯曲模量 [MPa]: 0.125
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.9115 g/cc | 0.03293 lb/in³ | AT Plastics PTM-03 |
| Melt Flow | 400 g/10 min @Load 0.325 kg, Temperature 125 °C | 400 g/10 min @Load 0.716 lb, Temperature 257 °F | Modified; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 95 | 95 | ASTM D2240 |
| Tensile Strength at Break | 7.50 MPa | 1090 psi | Type IV (50 mm/min); ASTM D638 |
| Elongation at Break | 110 % | 110 % | Type IV (50 mm/min); ASTM D638 |
| Flexural Modulus | 0.125 GPa | 18.1 ksi | 1% Secant; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 99.0 °C | 210 °F | DSC; ASTM D3417 |
| Ring & Ball Softening Point | 109 °C | 228 °F | ASTM E28 |