- 熔体流动速率 [g/10min]: 0.7
- 密度 [g/cm3]: 0.94
- 弯曲模量 [MPa]: 0.0480
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.940 g/cc | 0.0340 lb/in³ | ASTM D1505; ASTM D1928 Proc A |
| Vinyl Acetate Content | 18 % | 18 % | AT Plastics PTM-39 |
| Melt Flow | 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.70 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 92 | 92 | ASTM D2240 |
| Tensile Strength at Break | 26.8 MPa | 3890 psi | Type IV (50 mm/min); ASTM D638 |
| Elongation at Break | 700 % | 700 % | Type IV (50 mm/min); ASTM D638 |
| Flexural Modulus | 0.0480 GPa | 6.96 ksi | 1% Secant; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 87.0 °C | 189 °F | DSC; ASTM D3417 |
| Ring & Ball Softening Point | 220 °C | 428 °F | ASTM E28 |