- 熔体流动速率 [g/10min]: 150.0
- 密度 [g/cm3]: 0.945
- 弯曲模量 [MPa]: 0.0120
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.945 g/cc | 0.0341 lb/in³ | ASTM D1505; ASTM D1928 Proc A |
| Vinyl Acetate Content | 28 % | 28 % | AT Plastics PTM-39 |
| Melt Flow | 150 g/10 min @Load 0.325 kg, Temperature 125 °C | 150 g/10 min @Load 0.716 lb, Temperature 257 °F | Modified; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 74 | 74 | ASTM D2240 |
| Tensile Strength at Break | 5.50 MPa | 798 psi | Type IV (50 mm/min); ASTM D638 |
| Elongation at Break | 830 % | 830 % | Type IV (50 mm/min); ASTM D638 |
| Flexural Modulus | 0.0120 GPa | 1.74 ksi | 1% Secant; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Ring & Ball Softening Point | 91.0 °C | 196 °F | ASTM E28 |