- 熔体流动速率 [g/10min]: 12.0
- 密度 [g/cm3]: 0.916
- 弯曲模量 [MPa]: 0.220
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.916 g/cc | 0.0331 lb/in³ | AT Plastics PTM-03 | ||
| Thickness | >= 5.00 microns | >= 0.197 mil | Coating Thickness | ||
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 190 °C | 12 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Coating Weight | 4.80 g/m² | 3.00 lb/ream | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 94 | 94 | ASTM D2240 | ||
| Hardness, Shore D | 49 | 49 | ASTM D2240 | ||
| Tensile Strength at Break | 9.00 MPa | 1310 psi | Type IV (50 mm/min); ASTM D638 | ||
| Elongation at Break | 500 % | 500 % | Type IV (50 mm/min); ASTM D638 | ||
| Flexural Modulus | 0.220 GPa | 31.9 ksi | 1% Secant; ASTM D790 | ||
| Thermal Properties | Metric | English | Comments | ||
| Vicat Softening Point | 90.0 °C | 194 °F | ASTM D1525 | ||
| Descriptive Properties | |||||
| Line Speed ft/min | < 1500 | ||||