- 熔体流动速率 [g/10min]: 0.3
- 密度 [g/cm3]: 0.924
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in³ | AT Plastics PTM-03 |
| Thickness | 150 microns | 5.91 mil | |
| Melt Flow | 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.30 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 11.0 MPa | 1600 psi | Method A (500 mm/min); ASTM D882 |
| Film Tensile Strength at Yield, TD | 11.0 MPa | 1600 psi | Method A (500 mm/min); ASTM D882 |
| Film Elongation at Break, MD | 570 % | 570 % | Method A (500 mm/min); ASTM D882 |
| Film Elongation at Break, TD | 680 % | 680 % | Method A (500 mm/min); ASTM D882 |
| Secant Modulus, MD | 0.200 GPa | 29.0 ksi | 1% Secant Modulus; ASTM D882 |
| Secant Modulus, TD | 0.220 GPa | 31.9 ksi | 1% Secant Modulus; ASTM D882 |
| Film Tensile Strength at Break, MD | 21.0 MPa | 3050 psi | Method A (500 mm/min); ASTM D882 |
| Film Tensile Strength at Break, TD | 22.0 MPa | 3190 psi | Method A (500 mm/min); ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 13 % | 13 % | ASTM D1003 |
| Gloss | 77 % | 77 % | 45°; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 170 - 230 °C | 338 - 446 °F | |
| Blow-up Ratio (BUR) | 2.0 | 2.0 | |