- 熔体流动速率 [g/10min]: 220.0
- 密度 [g/cm3]: 0.935
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.935 g/cc | 0.0338 lb/in³ | ASTM D1505; ASTM D1928 Proc A |
| Vinyl Acetate Content | 13 % | 13 % | AT Plastics PTM-39 |
| Melt Flow | 220 g/10 min @Load 2.16 kg, Temperature 190 °C | 220 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 4.50 MPa | 653 psi | Type IV (50 mm/min); ASTM D638 |
| Elongation at Break | 200 % | 200 % | Type IV (50 mm/min); ASTM D638 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 89.0 °C | 192 °F | DSC; ASTM D3417 |