- 熔体流动速率 [g/10min]: 3.0
- 密度 [g/cm3]: 0.929
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.929 g/cc | 0.0336 lb/in³ | ISO 1183 |
| Thickness | 40.0 microns | 1.57 mil | |
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 3.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Antiblock Level | 550 ppm | 550 ppm | Additive - Synthetic Silica |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 250 % | 250 % | ISO 527-3 |
| Film Elongation at Break, TD | 580 % | 580 % | ISO 527-3 |
| Secant Modulus, MD | 0.230 GPa | 33.4 ksi | ASTM D882-A |
| Secant Modulus, TD | 0.260 GPa | 37.7 ksi | ASTM D882-A |
| Impact | 29 | 29 | Puncture Resistance, force (N); ASTM D5748 |
| Puncture Energy | 0.400 J | 0.295 ft-lb | ASTM D5748 |
| Coefficient of Friction, Dynamic | 0.40 | 0.40 | ISO 8295 |
| Tear Strength, Total | 2.50 N | 0.562 lb (f) | TD; ISO 6383/2 |
| 4.00 N | 0.899 lb (f) | MD; ISO 6383/2 | |
| Dart Drop | 2.00 g/micron | 50.8 g/mil | ISO 7765/1 |
| Film Tensile Strength at Break, MD | 22.0 MPa | 3190 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 20.0 MPa | 2900 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 116 °C | 241 °F | ISO 11357/03 |
| Vicat Softening Point | 102 °C | 216 °F | A (10N); ISO 306 |
| Optical Properties | Metric | English | Comments |
| Haze | 6.0 % | 6.0 % | ASTM D1003 |
| Gloss | 110 % | 110 % | ASTM D2457 |