- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.927
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.927 g/cc | 0.0335 lb/in³ | ISO 1183 |
| Thickness | 40.0 microns | 1.57 mil | |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Antiblock Level | 750 ppm | 750 ppm | Additive - Synthetic Silica |
| Slip Level | 300 ppm | 300 ppm | Additive - Erucamide |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 230 % | 230 % | ISO 527-3 |
| Film Elongation at Break, TD | 550 % | 550 % | ISO 527-3 |
| Secant Modulus, MD | 0.190 GPa | 27.6 ksi | ASTM D882-A |
| Secant Modulus, TD | 0.220 GPa | 31.9 ksi | ASTM D882-A |
| Impact | 33.5 | 33.5 | Puncture Resistance, force (N); ASTM D5748 |
| Puncture Energy | 0.500 J | 0.369 ft-lb | ASTM D5748 |
| Coefficient of Friction, Dynamic | 0.20 | 0.20 | ISO 8295 |
| Tear Strength, Total | 2.50 N | 0.562 lb (f) | TD; ISO 6383/2 |
| 4.00 N | 0.899 lb (f) | MD; ISO 6383/2 | |
| Dart Drop | 2.25 g/micron | 57.1 g/mil | ISO 7765/1 |
| Film Tensile Strength at Break, MD | 24.0 MPa | 3480 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 20.0 MPa | 2900 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 116 °C | 241 °F | ISO 11357/03 |
| Vicat Softening Point | 101 °C | 214 °F | A (10N); ISO 306 |
| Optical Properties | Metric | English | Comments |
| Haze | 6.0 % | 6.0 % | ASTM D1003 |
| Gloss | 105 % | 105 % | ASTM D2457 |