- 熔体流动速率 [g/10min]: 2.1
- 密度 [g/cm3]: 0.922
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.922 g/cc | 0.0333 lb/in³ | ISO 1183 |
| Melt Flow | 2.1 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.1 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 350 % | 350 % | ISO 527-3 |
| Film Elongation at Break, TD | 600 % | 600 % | ISO 527-3 |
| Tensile Modulus | 0.200 GPa | 29.0 ksi | MD; ASTM D882-A |
| 0.210 GPa | 30.5 ksi | TD; ASTM D882-A | |
| Puncture Energy | 1.30 J | 0.959 ft-lb | 50 N; 40µm sample; ASTM D5748 |
| Coefficient of Friction | 0.90 | 0.90 | Dynamic; ISO 8295 |
| Elmendorf Tear Strength, MD | 12.7 g/micron | 323 g/mil | ISO 6383/2 |
| Elmendorf Tear Strength, TD | 7.65 g/micron | 194 g/mil | ISO 6383/2 |
| Dart drop Test | 100 g @Thickness 0.0400 mm | 0.221 lb @Thickness 0.00157 in | ISO 7765-1 |
| Film Tensile Strength at Break, MD | 26.0 MPa | 3770 psi | ISO 527-2 |
| Film Tensile Strength at Break, TD | 20.0 MPa | 2900 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 111 °C | 232 °F | ISO 11357-3 |
| Vicat Softening Point | 95.0 °C | 203 °F | ISO 306 |
| Optical Properties | Metric | English | Comments |
| Haze | 7.0 % | 7.0 % | ASTM D1003 |
| Gloss | 85 % | 85 % | ASTM D2457 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 150 - 180 °C | 302 - 356 °F | |