- 熔体流动速率 [g/10min]: 0.48
- 密度 [g/cm3]: 0.92
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ASTM D1505 | ||
| Thickness | 38.0 microns | 1.50 mil | |||
| Melt Flow | 0.48 g/10 min @Load 2.16 kg, Temperature 230 °C | 0.48 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 15.0 MPa | 2180 psi | ASTM D638 | ||
| Film Elongation at Break, MD | 206 % | 206 % | ASTM D882 | ||
| Film Elongation at Break, TD | 1241 % | 1241 % | ASTM D882 | ||
| Elongation at Break | 617 % | 617 % | ASTM D638 | ||
| Coefficient of Friction | 0.090 | 0.090 | ASTM D1894 | ||
| Elmendorf Tear Strength, TD | 4.30 g/micron | 109 g/mil | ASTM D1922 | ||
| Dart Drop | 4.42 g/micron | 112 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 31.0 MPa | 4500 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 22.0 MPa | 3190 psi | ASTM D882 | ||
| Heat Seal Strength Initiation Temperature | 105 °C | 221 °F | Sealing Initial Temperature; Braskem® Method | ||
| Thermal Properties | Metric | English | Comments | ||
| Vicat Softening Point | 89.0 °C | 192 °F | ASTM D1525 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 7.0 % | 7.0 % | ASTM D1003 | ||
| Gloss | 9.0 % | 9.0 % | 60° angle; ASTM D2457 | ||
| Descriptive Properties | |||||
| Additives | Antiblock and Slip | ||||
| Minimum Recommended Thickness | 40 µm | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.
Users of our Advanced Search (registration required) may exclude discontinued materials from search results.