- 熔体流动速率 [g/10min]: 1.2
- 密度 [g/cm3]: 0.922
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.922 g/cc | 0.0333 lb/in³ | ISO 1183 |
| Melt Flow | 1.2 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.2 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Antiblock Level | 850 ppm | 850 ppm | talc; Borealis Method |
| Slip Level | 450 ppm | 450 ppm | erucamide; Borealis Method |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 300 % | 300 % | ISO 527-3 |
| Film Elongation at Break, TD | 500 % | 500 % | ISO 527-3 |
| Tensile Modulus | 0.180 GPa | 26.1 ksi | MD/TD; ASTM D882-A |
| Puncture Energy | 2.00 J | 1.48 ft-lb | 53 N; 40µm sample; ASTM D5748 |
| Coefficient of Friction | 0.15 | 0.15 | Dynamic; ISO 8295 |
| Elmendorf Tear Strength, MD | 10.19 g/micron | 258.8 g/mil | ISO 6383/2 |
| Elmendorf Tear Strength, TD | 5.096 g/micron | 129.4 g/mil | ISO 6383/2 |
| Dart drop Test | 140 g @Thickness 0.0400 mm | 0.309 lb @Thickness 0.00157 in | ISO 7765-1 |
| Film Tensile Strength at Break, MD | 26.0 MPa | 3770 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 23.0 MPa | 3340 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 110 °C | 230 °F | ISO 11357-3 |
| Vicat Softening Point | 96.0 °C | 205 °F | ISO 306 |
| Optical Properties | Metric | English | Comments |
| Haze | 8.0 % | 8.0 % | ASTM D1003 |
| Gloss | 85 % | 85 % | ASTM D2457 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 160 - 190 °C | 320 - 374 °F | |