- 熔体流动速率 [g/10min]: 3.8
- 密度 [g/cm3]: 0.922
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.922 g/cc | 0.0333 lb/in³ | ASTM D1505 | ||
| Thickness | 38.0 microns | 1.50 mil | |||
| Melt Flow | 3.8 g/10 min @Load 2.16 kg, Temperature 230 °C | 3.8 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | ASTM D638 | ||
| Film Elongation at Break, MD | 391 % | 391 % | ASTM D882 | ||
| Film Elongation at Break, TD | 1217 % | 1217 % | ASTM D882 | ||
| Elongation at Break | 624 % | 624 % | ASTM D638 | ||
| Coefficient of Friction | 0.10 | 0.10 | ASTM D1894 | ||
| Elmendorf Tear Strength, TD | 3.80 g/micron | 96.5 g/mil | ASTM D1922 | ||
| Dart Drop | 1.94 g/micron | 49.3 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 22.0 MPa | 3190 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 17.0 MPa | 2470 psi | ASTM D882 | ||
| Heat Seal Strength Initiation Temperature | 105 °C | 221 °F | Sealing Initial Temperature; Braskem® Method | ||
| Thermal Properties | Metric | English | Comments | ||
| Vicat Softening Point | 89.0 °C | 192 °F | ASTM D1525 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 5.4 % | 5.4 % | ASTM D1003 | ||
| Gloss | 12 % | 12 % | 60° angle; ASTM D2457 | ||
| Descriptive Properties | |||||
| Additives | Antiblock and Slip | ||||
| Minimum Recommended Thickness | 25 µm | ||||