Braskem TS7010 LDPE Blown Film Extrusion Polyethylene

Braskem TS7010 LDPE Blown Film Extrusion Polyethylene 物性表: Braskem TS7010 LDPE Blown Film Extrusion Polyethylene物性表及特性介绍,Braskem TS7010 LDPE Blown Film Extrusion Polyethylene注塑参数详情,如需Braskem TS7010 LDPE Blown Film Extrusion Polyethylene下载, 可到相关下载区下载
  • 熔体流动速率 [g/10min]: 1.0
  • 密度 [g/cm3]: 0.922
 
Physical PropertiesMetricEnglishComments
Density 0.922 g/cc0.0333 lb/in³ASTM-D792
Melt Flow 1.0 g/10 min
@Load 2.16 kg,
Temperature 190 °C
1.0 g/10 min
@Load 4.76 lb,
Temperature 374 °F
ASTM-D1238
 
Mechanical PropertiesMetricEnglishComments
Film Elongation at Break, MD 350 %350 %ASTM-D882
Film Elongation at Break, TD 620 %620 %ASTM-D882
Secant Modulus, MD 0.120 GPa17.4 ksi2% Secant Modulus; ASTM-D882
Secant Modulus, TD 0.130 GPa18.9 ksi2% Secant Modulus; ASTM-D882
Elmendorf Tear Strength MD 310 g310 gASTM-D1922
Elmendorf Tear Strength TD 240 g240 gASTM-D1922
Elmendorf Tear Strength, MD 6.20 g/micron157 g/milASTM-D1922
Elmendorf Tear Strength, TD 4.80 g/micron122 g/milASTM-D1922
Dart Drop 3.40 g/micron86.4 g/milASTM-D1709
Dart drop Test 170 g0.375 lbASTM-D1709
Film Tensile Strength at Break, MD 23.0 MPa3340 psiASTM-D882
Film Tensile Strength at Break, TD 21.0 MPa3050 psiASTM-D882
 
Optical PropertiesMetricEnglishComments
Haze 9.5 %9.5 %ASTM-D1003
Gloss 58 %58 %Angle 45°; ASTM-D2457
 85 %85 %Angle 60°; ASTM-D2457
 
Processing PropertiesMetricEnglishComments
Die Opening 0.100 cm0.0394 inBlow Film Extrusion
Blow-up Ratio (BUR) 2.0 - 3.02.0 - 3.0Blow Film Extrusion
 
Descriptive Properties
Mass Temperature (°C)175-185Blow Film Extrusion
Temperature Profile (°C)155-185Blow Film Extrusion

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-40968.html

免责声明: 本文 Braskem TS7010 LDPE Blown Film Extrusion Polyethylene 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4