- 熔体流动速率 [g/10min]: 0.27
- 密度 [g/cm3]: 0.929
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.929 g/cc | 0.0336 lb/in³ | ASTM-D792 | ||
| Melt Flow | 0.27 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.27 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 370 % | 370 % | ASTM-D882 | ||
| Film Elongation at Break, TD | 700 % | 700 % | ASTM-D882 | ||
| Secant Modulus, MD | 0.170 GPa | 24.7 ksi | 2% Secant Modulus; ASTM-D882 | ||
| Secant Modulus, TD | 0.180 GPa | 26.1 ksi | 2% Secant Modulus; ASTM-D882 | ||
| Elmendorf Tear Strength MD | 210 g | 210 g | ASTM-D1922 | ||
| Elmendorf Tear Strength TD | 260 g | 260 g | ASTM-D1922 | ||
| Elmendorf Tear Strength, MD | 4.20 g/micron | 107 g/mil | ASTM-D1922 | ||
| Elmendorf Tear Strength, TD | 5.20 g/micron | 132 g/mil | ASTM-D1922 | ||
| Dart Drop | 2.40 g/micron | 61.0 g/mil | ASTM-D1709 | ||
| Dart drop Test | 120 g | 0.265 lb | ASTM-D1709 | ||
| Film Tensile Strength at Break, MD | 25.0 MPa | 3630 psi | ASTM-D882 | ||
| Film Tensile Strength at Break, TD | 24.0 MPa | 3480 psi | ASTM-D882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 12 % | 12 % | ASTM-D1003 | ||
| Gloss | 53 % | 53 % | Angle 45°; ASTM-D2457 | ||
| 79 % | 79 % | Angle 60°; ASTM-D2457 | |||
| Processing Properties | Metric | English | Comments | ||
| Die Opening | 0.100 cm | 0.0394 in | Blow Film Extrusion | ||
| Blow-up Ratio (BUR) | 2.0 - 3.0 | 2.0 - 3.0 | Blow Film Extrusion | ||
| Descriptive Properties | |||||
| Mass Temperature (°C) | 180-220 | Blow Film Extrusion | |||
| Temperature Profile (°C) | 150-195 | Blow Film Extrusion | |||