- 熔体流动速率 [g/10min]: 30.0
- 拉伸强度 [MPa]: 8.0
- 弯曲模量 [MPa]: 450
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.915 g/cc | 0.915 g/cc | ASTM D1505/D792 |
| ESCR 10% Igepal® | 15 hour @Temperature 50.0 °C | 15 hour @Temperature 122 °F | h/50%f; compression molded 2 mm notched-plaques; ASTM D1683 |
| Melt Flow | 30 g/10 min @Load 2.16 kg, Temperature 190 °C | 30 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 39 | 39 | ASTM D2240 |
| Tensile Strength at Break | 8.00 MPa | 1160 psi | ASTM D638 |
| Tensile Strength, Yield | 8.00 MPa | 1160 psi | ASTM D638 |
| Flexural Modulus, 1% Secant | 450 MPa | 65300 psi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 79.0 °C | 174 °F | ASTM D1525 |