- 熔体流动速率 [g/10min]: 0.14
- 密度 [g/cm3]: 0.923
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.923 g/cc | 0.0333 lb/in³ | ASTM-D792 | ||
| Melt Flow | 0.14 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.14 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 500 % | 500 % | ASTM-D882 | ||
| Film Elongation at Break, TD | 710 % | 710 % | ASTM-D882 | ||
| Secant Modulus, MD | 0.0950 GPa | 13.8 ksi | 2% Secant Modulus; ASTM-D882 | ||
| Secant Modulus, TD | 0.0900 GPa | 13.1 ksi | 2% Secant Modulus; ASTM-D882 | ||
| Elmendorf Tear Strength MD | 470 g | 470 g | ASTM-D1922 | ||
| Elmendorf Tear Strength TD | 700 g | 700 g | ASTM-D1922 | ||
| Elmendorf Tear Strength, MD | 3.13 g/micron | 79.5 g/mil | ASTM-D1922 | ||
| Elmendorf Tear Strength, TD | 4.67 g/micron | 119 g/mil | ASTM-D1922 | ||
| Dart Drop | 2.73 g/micron | 69.3 g/mil | ASTM-D1709 (Method B) | ||
| Dart drop Test | 410 g | 0.904 lb | ASTM-D1709 (Method B) | ||
| Film Tensile Strength at Break, MD | 18.0 MPa | 2610 psi | ASTM-D882 | ||
| Film Tensile Strength at Break, TD | 22.0 MPa | 3190 psi | ASTM-D882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 16 % | 16 % | ASTM-D1003 | ||
| Gloss | 62 % | 62 % | Angle 60°; ASTM-D2457 | ||
| Transmission, Visible | 90.0 % | 90.0 % | transparent; thickness not quantified | ||
| Processing Properties | Metric | English | Comments | ||
| Die Opening | 0.100 - 0.150 cm | 0.0394 - 0.0591 in | Blow Film Extrusion | ||
| Blow-up Ratio (BUR) | 2.0 - 3.0 | 2.0 - 3.0 | Blow Film Extrusion | ||
| Descriptive Properties | |||||
| Mass Temperature (°C) | 190-225 | Blow Film Extrusion | |||
| Temperature Profile (°C) | 170-225 | Blow Film Extrusion | |||
| UV Stabilizer (ppm) | 5750-6500 | Braskem PE-6 | |||