- 熔体流动速率 [g/10min]: 30.0
- 密度 [g/cm3]: 0.918
- 拉伸强度 [MPa]: 9.0
- 弯曲模量 [MPa]: 200
- 脆化温度 [℃]: -70.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ASTM-D792 | ||
| ESCR 10% Igepal® | 1.0 hour @Thickness 2.00 mm, Temperature 50.0 °C | 1.0 hour @Thickness 0.0787 in, Temperature 122 °F | 0.3 mm notched-plaques; ASTM-D1693 | ||
| Melt Flow | 30 g/10 min @Load 2.16 kg, Temperature 190 °C | 30 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 40 | 40 | ASTM-D2240 | ||
| Tensile Strength at Break | 6.00 MPa | 870 psi | ASTM-D638 | ||
| Tensile Strength, Yield | 9.00 MPa | 1310 psi | ASTM-D638 | ||
| Elongation at Break | 150 % | 150 % | ASTM-D638 | ||
| Modulus of Rigidity | 0.320 GPa | 46.4 ksi | ASTM-D747 | ||
| Flexural Modulus, 1% Secant | 200 MPa | 29000 psi | ASTM-D790 | ||
| Thermal Properties | Metric | English | Comments | ||
| Vicat Softening Point | 85.0 °C @Load 1.02 kg | 185 °F @Load 2.25 lb | ASTM-D1525 | ||
| Brittleness Temperature | -70.0 °C | -94.0 °F | ASTM-D746 | ||
| Descriptive Properties | |||||
| Temperature Profile (°C) | 130-170 | Injection Molding | |||