- 熔体流动速率 [g/10min]: 0.12
- 密度 [g/cm3]: 0.922
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.922 g/cc | 0.0333 lb/in³ | ASTM-D792 | ||
| Melt Flow | 0.12 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.12 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 360 % | 360 % | ASTM-D882 | ||
| Film Elongation at Break, TD | 740 % | 740 % | ASTM-D882 | ||
| Secant Modulus, MD | 0.150 GPa | 21.8 ksi | 2% Secant Modulus; ASTM-D882 | ||
| Secant Modulus, TD | 0.170 GPa | 24.7 ksi | 2% Secant Modulus; ASTM-D882 | ||
| Elmendorf Tear Strength MD | 180 g | 180 g | ASTM-D1922 | ||
| Elmendorf Tear Strength TD | 200 g | 200 g | ASTM-D1922 | ||
| Elmendorf Tear Strength, MD | 3.60 g/micron | 91.4 g/mil | ASTM-D1922 | ||
| Elmendorf Tear Strength, TD | 4.00 g/micron | 102 g/mil | ASTM-D1922 | ||
| Dart Drop | 4.00 g/micron | 102 g/mil | ASTM-D1709 | ||
| Dart drop Test | 200 g | 0.441 lb | ASTM-D1709 | ||
| Film Tensile Strength at Break, MD | 28.0 MPa | 4060 psi | ASTM-D882 | ||
| Film Tensile Strength at Break, TD | 26.0 MPa | 3770 psi | ASTM-D882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 19 % | 19 % | ASTM-D1003 | ||
| Gloss | 33 % | 33 % | Angle 45°; ASTM-D2457 | ||
| 53 % | 53 % | Angle 60°; ASTM-D2457 | |||
| Processing Properties | Metric | English | Comments | ||
| Die Opening | 0.100 - 0.150 cm | 0.0394 - 0.0591 in | Blow Film Extrusion | ||
| Blow-up Ratio (BUR) | 2.0 - 3.0 | 2.0 - 3.0 | Blow Film Extrusion | ||
| Descriptive Properties | |||||
| Mass Temperature (°C) | 190-225 | Blow Film Extrusion | |||
| Temperature Profile (°C) | 170-225 | Blow Film Extrusion | |||