- 熔体流动速率 [g/10min]: 1.2
- 密度 [g/cm3]: 0.922
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.922 g/cc | 0.0333 lb/in³ | ASTM-D792 | ||
| Melt Flow | 1.2 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.2 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 350 % | 350 % | ASTM-D882 | ||
| Film Elongation at Break, TD | 680 % | 680 % | ASTM-D882 | ||
| Secant Modulus, MD | 0.120 GPa | 17.4 ksi | 2% Secant Modulus; ASTM-D882 | ||
| Secant Modulus, TD | 0.140 GPa | 20.3 ksi | 2% Secant Modulus; ASTM-D882 | ||
| Elmendorf Tear Strength MD | 360 g | 360 g | ASTM-D1922 | ||
| Elmendorf Tear Strength TD | 260 g | 260 g | ASTM-D1922 | ||
| Elmendorf Tear Strength, MD | 7.20 g/micron | 183 g/mil | ASTM-D1922 | ||
| Elmendorf Tear Strength, TD | 5.20 g/micron | 132 g/mil | ASTM-D1922 | ||
| Dart Drop | 3.20 g/micron | 81.3 g/mil | ASTM-D1709 | ||
| Dart drop Test | 160 g | 0.353 lb | ASTM-D1709 | ||
| Film Tensile Strength at Break, MD | 23.0 MPa | 3340 psi | ASTM-D882 | ||
| Film Tensile Strength at Break, TD | 21.0 MPa | 3050 psi | ASTM-D882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 8.5 % | 8.5 % | ASTM-D1003 | ||
| Gloss | 60 % | 60 % | Angle 45°; ASTM-D2457 | ||
| 88 % | 88 % | Angle 60°; ASTM-D2457 | |||
| Processing Properties | Metric | English | Comments | ||
| Die Opening | 0.100 cm | 0.0394 in | Blow Film Extrusion | ||
| Blow-up Ratio (BUR) | 2.0 - 3.0 | 2.0 - 3.0 | Blow Film Extrusion | ||
| Descriptive Properties | |||||
| Mass Temperature (°C) | 175-185 | Blow Film Extrusion | |||
| Temperature Profile (°C) | 150-185 | Blow Film Extrusion | |||