- 密度 [g/cm3]: 0.922
- 拉伸强度 [MPa]: 11.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.922 - 0.924 g/cc | 0.0333 - 0.0334 lb/in³ | ASTM D1505 |
| Thickness | 50.0 microns | 1.97 mil | |
| Melt Index of Compound | 2.2 - 2.9 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.2 - 2.9 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 12.5 MPa | 1810 psi | ASTM D638 |
| Tensile Strength, Yield | 11.0 MPa | 1600 psi | ASTM D638 |
| Film Elongation at Break, MD | 400 % | 400 % | ASTM D882 |
| Film Elongation at Break, TD | 690 % | 690 % | ASTM D882 |
| Elongation at Break | 575 % | 575 % | ASTM D638 |
| Secant Modulus, MD | 0.0970 GPa | 14.1 ksi | 5%; ASTM D882 |
| Secant Modulus, TD | 0.105 GPa | 15.2 ksi | 5%; ASTM D882 |
| Coefficient of Friction, Dynamic | 0.10 | 0.10 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 9.00 g/micron | 229 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 6.20 g/micron | 157 g/mil | ASTM D1922 |
| Dart drop Test | 135 g | 0.298 lb | (method A); ASTM D1709 |
| Film Tensile Strength at Break, MD | 20.0 MPa | 2900 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 18.0 MPa | 2610 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 94.0 °C | 201 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 7.9 % | 7.9 % | ASTM D1003 |
| Gloss | 103 % | 103 % | @ 60° Gardner; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 150 - 160 °C | 302 - 320 °F | Plasticizing Zone |
| 160 - 170 °C | 320 - 338 °F | Mixture Zone | |
| Feed Temperature | 140 - 150 °C | 284 - 302 °F | |
| Adapter Temperature | 165 - 175 °C | 329 - 347 °F | |
| Blow-up Ratio (BUR) | 3.0 | 3.0 | Recommended |