- 熔体流动速率 [g/10min]: 5.5
- 密度 [g/cm3]: 0.916
- 缺口冲击强度: 48.0
- 拉伸强度 [MPa]: 9.0
- 弯曲强度 [MPa]: 10.3
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.916 g/cc | 0.0331 lb/in³ | |
| Melt Flow | 5.5 g/10 min @Load 2.16 kg | 5.5 g/10 min @Load 4.76 lb | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 10.3 MPa | 1490 psi | |
| Tensile Strength, Yield | 9.00 MPa | 1310 psi | |
| Elongation at Break | 600 % | 600 % | |
| Modulus of Elasticity | 0.172 GPa | 24.9 ksi | Molded Sample 2% Secant Modulus |
| Izod Impact, Notched (ISO) | 48.0 kJ/m² @Temperature -50.0 °C | 22.8 ft-lb/in² @Temperature -58.0 °F | |
| Tensile Impact Strength | 275 kJ/m² | 131 ft-lb/in² | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 90.0 °C | 194 °F | |