- 熔体流动速率 [g/10min]: 3.3
- 密度 [g/cm3]: 0.912
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.912 g/cc | 0.0329 lb/in³ | |
| Thickness | 25.0 microns | 0.984 mil | |
| Melt Flow | 3.3 g/10 min @Load 2.16 kg | 3.3 g/10 min @Load 4.76 lb | Melt flow ratio I10/I2 is 7.7. |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 6.90 MPa | 1000 psi | |
| Film Tensile Strength at Yield, TD | 6.20 MPa | 899 psi | |
| Film Elongation at Break, MD | 580 % | 580 % | |
| Film Elongation at Break, TD | 780 % | 780 % | |
| Elmendorf Tear Strength MD | 400 g | 400 g | |
| Elmendorf Tear Strength TD | 590 g | 590 g | |
| Elmendorf Tear Strength, MD | 16.0 g/micron | 406 g/mil | |
| Elmendorf Tear Strength, TD | 23.6 g/micron | 599 g/mil | |
| Dart Drop | 18.4 g/micron | 467 g/mil | |
| Film Tensile Strength at Break, MD | 56.5 MPa | 8190 psi | |
| Film Tensile Strength at Break, TD | 36.5 MPa | 5290 psi | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 90.0 °C | 194 °F | |
| Optical Properties | Metric | English | Comments |
| Haze | 0.80 % | 0.80 % | |
| Gloss | 95 % | 95 % | 45° |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 274 °C | 525 °F | Film extrusion temperature |