- 熔体流动速率 [g/10min]: 12.0
- 密度 [g/cm3]: 0.916
- 缺口冲击强度: 27.0
- 拉伸强度 [MPa]: 9.17
- 弯曲强度 [MPa]: 10.6
- 弯曲模量 [MPa]: 0.237
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.916 g/cc | 0.0331 lb/in³ | |
| Melt Flow | 12 g/10 min @Load 2.16 kg | 12 g/10 min @Load 4.76 lb | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 10.6 MPa | 1540 psi | |
| Tensile Strength, Yield | 9.17 MPa | 1330 psi | |
| Elongation at Break | 100 % | 100 % | |
| Modulus of Elasticity | 0.153 GPa | 22.2 ksi | Molded Sample 2% Secant Modulus |
| Flexural Modulus | 0.237 GPa | 34.4 ksi | |
| Izod Impact, Notched (ISO) | 27.0 kJ/m² @Temperature -50.0 °C | 12.8 ft-lb/in² @Temperature -58.0 °F | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 90.0 °C | 194 °F | |