- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.923
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.923 g/cc | 0.0333 lb/in³ | |
| Thickness | 40.0 microns | 1.57 mil | |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg | 1.0 g/10 min @Load 4.76 lb | |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 10.0 MPa | 1450 psi | |
| Film Tensile Strength at Yield, TD | 9.70 MPa | 1410 psi | |
| Film Elongation at Break, MD | 370 % | 370 % | |
| Film Elongation at Break, TD | 510 % | 510 % | |
| Coefficient of Friction | 0.50 | 0.50 | |
| Elmendorf Tear Strength MD | 430 g | 430 g | |
| Elmendorf Tear Strength TD | 280 g | 280 g | |
| Elmendorf Tear Strength, MD | 10.8 g/micron | 274 g/mil | |
| Elmendorf Tear Strength, TD | 7.00 g/micron | 178 g/mil | |
| Dart Drop | 2.50 g/micron | 63.5 g/mil | |
| Film Tensile Strength at Break, MD | 21.4 MPa | 3100 psi | |
| Film Tensile Strength at Break, TD | 15.2 MPa | 2200 psi | |
| Optical Properties | Metric | English | Comments |
| Haze | 11 % | 11 % | |
| Gloss | 55 % | 55 % | 45° |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 204 °C | 399 °F | Film extrusion temperature |