- 熔体流动速率 [g/10min]: 1.2
- 密度 [g/cm3]: 0.922
- 拉伸强度 [MPa]: 8.3
- 弯曲强度 [MPa]: 12.4
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.922 g/cc | 0.0333 lb/in³ | |
| Thickness | 40.0 microns | 1.57 mil | |
| Melt Flow | 1.2 g/10 min @Load 2.16 kg | 1.2 g/10 min @Load 4.76 lb | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 12.4 MPa | 1800 psi | Molded property |
| Film Tensile Strength at Yield, MD | 11.7 MPa | 1700 psi | |
| Film Tensile Strength at Yield, TD | 10.7 MPa | 1550 psi | |
| Tensile Strength, Yield | 8.30 MPa | 1200 psi | Molded property |
| Film Elongation at Break, MD | 425 % | 425 % | |
| Film Elongation at Break, TD | 600 % | 600 % | |
| Elongation at Break | 625 % | 625 % | Molded value |
| Coefficient of Friction | 0.70 | 0.70 | |
| Elmendorf Tear Strength MD | 175 g | 175 g | |
| Elmendorf Tear Strength TD | 225 g | 225 g | |
| Elmendorf Tear Strength, MD | 4.40 g/micron | 112 g/mil | |
| Elmendorf Tear Strength, TD | 5.60 g/micron | 142 g/mil | |
| Dart Drop | 3.00 g/micron | 76.2 g/mil | |
| Film Tensile Strength at Break, MD | 29.0 MPa | 4210 psi | |
| Film Tensile Strength at Break, TD | 20.0 MPa | 2900 psi | |
| Optical Properties | Metric | English | Comments |
| Haze | 6.0 % | 6.0 % | |
| Gloss | 65 % | 65 % | 45° |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 177 °C | 351 °F | Film extrusion temperature |