- 熔体流动速率 [g/10min]: 0.9
- 密度 [g/cm3]: 0.924
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in³ | |
| Thickness | 30.0 microns | 1.18 mil | |
| Melt Flow | 0.90 g/10 min @Load 2.16 kg | 0.90 g/10 min @Load 4.76 lb | |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 11.9 MPa | 1730 psi | |
| Film Tensile Strength at Yield, TD | 12.1 MPa | 1750 psi | |
| Film Elongation at Break, MD | 310 % | 310 % | |
| Film Elongation at Break, TD | 590 % | 590 % | |
| Coefficient of Friction | 0.20 | 0.20 | |
| Elmendorf Tear Strength MD | 370 g | 370 g | |
| Elmendorf Tear Strength TD | 240 g | 240 g | |
| Elmendorf Tear Strength, MD | 12.3 g/micron | 312 g/mil | |
| Elmendorf Tear Strength, TD | 8.00 g/micron | 203 g/mil | |
| Dart Drop | 2.70 g/micron | 68.6 g/mil | |
| Film Tensile Strength at Break, MD | 24.1 MPa | 3500 psi | |
| Film Tensile Strength at Break, TD | 19.8 MPa | 2870 psi | |
| Optical Properties | Metric | English | Comments |
| Haze | 4.4 % | 4.4 % | |
| Gloss | 75 % | 75 % | 45° |
| Transmission, Visible | 90.0 % | 90.0 % | clear; thickness not quantified |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 193 °C | 379 °F | Film extrusion temperature |