- 熔体流动速率 [g/10min]: 1.9
- 密度 [g/cm3]: 0.926
- 拉伸强度 [MPa]: 12.4
- 弯曲强度 [MPa]: 10.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.926 g/cc | 0.0335 lb/in³ | |
| Thickness | 40.0 microns | 1.57 mil | |
| Melt Flow | 1.9 g/10 min @Load 2.16 kg | 1.9 g/10 min @Load 4.76 lb | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 10.0 MPa | 1450 psi | Molded property |
| Film Tensile Strength at Yield, MD | 12.4 MPa | 1800 psi | |
| Film Tensile Strength at Yield, TD | 12.6 MPa | 1830 psi | |
| Tensile Strength, Yield | 12.4 MPa | 1800 psi | Molded property |
| Film Elongation at Break, MD | 420 % | 420 % | |
| Film Elongation at Break, TD | 585 % | 585 % | |
| Elongation at Break | 500 % | 500 % | Molded value |
| Coefficient of Friction | 1.0 | 1.0 | |
| Elmendorf Tear Strength MD | 145 g | 145 g | |
| Elmendorf Tear Strength TD | 210 g | 210 g | |
| Elmendorf Tear Strength, MD | 3.60 g/micron | 91.4 g/mil | |
| Elmendorf Tear Strength, TD | 5.30 g/micron | 135 g/mil | |
| Dart Drop | 1.60 g/micron | 40.6 g/mil | |
| Film Tensile Strength at Break, MD | 26.7 MPa | 3870 psi | |
| Film Tensile Strength at Break, TD | 19.5 MPa | 2830 psi | |
| Optical Properties | Metric | English | Comments |
| Haze | 6.0 % | 6.0 % | |
| Gloss | 50 % | 50 % | 45° |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 177 °C | 351 °F | Film extrusion temperature |