- 熔体流动速率 [g/10min]: 8.0
- 密度 [g/cm3]: 0.916
- 缺口冲击强度: 28.0
- 拉伸强度 [MPa]: 8.9
- 弯曲强度 [MPa]: 11.0
- 弯曲模量 [MPa]: 0.226
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.916 g/cc | 0.0331 lb/in³ | |
| Viscosity | 34000 cP @Shear Rate 5000 1/s, Temperature 190 °C | 34000 cP @Shear Rate 5000 1/s, Temperature 374 °F | Apparent Dynamic Viscosity |
| 76000 cP @Shear Rate 1000 1/s, Temperature 190 °C | 76000 cP @Shear Rate 1000 1/s, Temperature 374 °F | Apparent Dynamic Viscosity | |
| 130000 cP @Shear Rate 300 1/s, Temperature 190 °C | 130000 cP @Shear Rate 300 1/s, Temperature 374 °F | Apparent Dynamic Viscosity | |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg | 8.0 g/10 min @Load 4.76 lb | Melt flow ratio I10/I2 is 9.3. |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 11.0 MPa | 1600 psi | |
| Tensile Strength, Yield | 8.90 MPa | 1290 psi | |
| Elongation at Break | 130 % | 130 % | |
| Modulus of Elasticity | 0.139 GPa | 20.2 ksi | Molded Sample 2% Secant Modulus |
| Flexural Modulus | 0.226 GPa | 32.8 ksi | |
| Izod Impact, Notched (ISO) | 28.0 kJ/m² @Temperature -50.0 °C | 13.3 ft-lb/in² @Temperature -58.0 °F | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 91.0 °C | 196 °F | |