- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.922
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.922 g/cc | 0.0333 lb/in³ | |
| Thickness | 30.0 microns | 1.18 mil | |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg | 2.0 g/10 min @Load 4.76 lb | |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 11.4 MPa | 1650 psi | |
| Film Tensile Strength at Yield, TD | 10.3 MPa | 1490 psi | |
| Film Elongation at Break, MD | 395 % | 395 % | |
| Film Elongation at Break, TD | 530 % | 530 % | |
| Coefficient of Friction | 0.70 | 0.70 | |
| Elmendorf Tear Strength MD | 410 g | 410 g | |
| Elmendorf Tear Strength TD | 250 g | 250 g | |
| Elmendorf Tear Strength, MD | 13.7 g/micron | 348 g/mil | |
| Elmendorf Tear Strength, TD | 8.30 g/micron | 211 g/mil | |
| Dart Drop | 3.20 g/micron | 81.3 g/mil | |
| Film Tensile Strength at Break, MD | 29.6 MPa | 4290 psi | |
| Film Tensile Strength at Break, TD | 17.9 MPa | 2600 psi | |
| Optical Properties | Metric | English | Comments |
| Haze | 7.5 % | 7.5 % | |
| Gloss | 63 % | 63 % | 45° |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 191 °C | 376 °F | Film extrusion temperature |