- 熔体流动速率 [g/10min]: 15.0
- 拉伸强度 [MPa]: 10.0
- 弯曲模量 [MPa]: 0.120
- 脆化温度 [℃]: -40.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.918 g/cc | 0.918 g/cc | ISO 1183 |
| Melt Flow | 15 g/10 min @Load 2.16 kg, Temperature 190 °C | 15 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 46 | 46 | ISO 868/A |
| Tensile Strength, Yield | 10.0 MPa | 1450 psi | ISO 527 |
| Flexural Modulus | 0.120 GPa | 17.4 ksi | ISO 178 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 108 °C | 226 °F | Internal method |
| Vicat Softening Point | 84.0 °C @Load 1.00 kg | 183 °F @Load 2.20 lb | ISO 306/A |
| Brittleness Temperature | <= -40.0 °C | <= -40.0 °F | ASTM D746 |