- 熔体流动速率 [g/10min]: 0.4
- 拉伸强度 [MPa]: 12.5
- 弯曲模量 [MPa]: 0.200
- 脆化温度 [℃]: -75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.925 g/cc | 0.925 g/cc | ISO 1183 |
| Melt Flow | 0.40 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.40 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 48 | 48 | ISO 868/A |
| Tensile Strength at Break | 18.0 MPa | 2610 psi | ISO 527 |
| Tensile Strength, Yield | 12.5 MPa | 1810 psi | ISO 527 |
| Elongation at Break | 550 % | 550 % | ISO 527 |
| Flexural Modulus | 0.200 GPa | 29.0 ksi | ISO 178 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 115 °C | 239 °F | Internal method |
| Vicat Softening Point | 100 °C @Load 1.00 kg | 212 °F @Load 2.20 lb | ISO 306/A |
| Brittleness Temperature | <= -75.0 °C | <= -103 °F | ASTM D746 |