- 熔体流动速率 [g/10min]: 13.0
- 拉伸强度 [MPa]: 4.0
- 弯曲模量 [MPa]: 0.0450
- 脆化温度 [℃]: -70.0
- 透光率 [%]: 90.0
Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 0.895 g/cc | 0.895 g/cc | ISO 1183 |
Melt Flow | 13 g/10 min @Load 2.16 kg, Temperature 190 °C | 13 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
Mechanical Properties | Metric | English | Comments |
Hardness, Shore D | 26 | 26 | ISO 868/A |
Tensile Strength at Break | 9.00 MPa | 1310 psi | ISO 527 |
Tensile Strength, Yield | 4.00 MPa | 580 psi | ISO 527 |
Elongation at Break | 750 % | 750 % | ISO 527 |
Flexural Modulus | 0.0450 GPa | 6.53 ksi | ISO 178 |
Thermal Properties | Metric | English | Comments |
Melting Point | 111 °C | 232 °F | Internal method |
Vicat Softening Point | 51.0 °C @Load 1.00 kg | 124 °F @Load 2.20 lb | ISO 306/A |
Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D746 |
Optical Properties | Metric | English | Comments |
Transmission, Visible | 90.0 % | 90.0 % | clear; thickness not quantified |