- 熔体流动速率 [g/10min]: 4.0
- 拉伸强度 [MPa]: 11.0
- 脆化温度 [℃]: -75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.923 g/cc | 0.923 g/cc | ISO 1183 |
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 4.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 48 | 48 | ISO 868/A |
| Tensile Strength at Break | 13.0 MPa | 1890 psi | ISO 527 |
| Tensile Strength, Yield | 11.0 MPa | 1600 psi | ISO 527 |
| Elongation at Break | 450 % | 450 % | ISO 527 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 113 °C | 235 °F | Internal method |
| Vicat Softening Point | 94.0 °C @Load 1.00 kg | 201 °F @Load 2.20 lb | ISO 306/A |
| Brittleness Temperature | <= -75.0 °C | <= -103 °F | ASTM D746 |