- 熔体流动速率 [g/10min]: 3.5
- 脆化温度 [℃]: -75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.933 g/cc | 0.933 g/cc | ISO 1183 |
| Thickness | 18.0 - 50.0 microns | 0.709 - 1.97 mil | Recommended |
| Melt Flow | 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C | 3.5 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 14.0 MPa | 2030 psi | ISO 527-3 |
| Film Tensile Strength at Yield, TD | 15.0 MPa | 2180 psi | ISO 527-3 |
| Film Elongation at Break, MD | 350 % | 350 % | ISO 527-3 |
| Film Elongation at Break, TD | 600 % | 600 % | ISO 527-3 |
| Coefficient of Friction, Dynamic | >= 0.50 | >= 0.50 | ISO 8295 |
| Elmendorf Tear Strength, MD | 5.095 g/micron | 129.4 g/mil | ISO 6383-2 |
| Elmendorf Tear Strength, TD | 6.6235 g/micron | 168.24 g/mil | ISO 6383-2 |
| Dart drop Test | 80.0 g | 0.176 lb | F50; ISO 7765-1 |
| Film Tensile Strength at Break, MD | 21.0 MPa | 3050 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 20.0 MPa | 2900 psi | ISO 527-3 |
| 1% Secant Modulus, MD | 300 MPa | 43500 psi | ISO 527-3 |
| 1% Secant Modulus, TD | 310 MPa | 45000 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 118 °C | 244 °F | Internal method |
| Vicat Softening Point | 107 °C @Load 1.00 kg | 225 °F @Load 2.20 lb | ISO 306/A |
| Brittleness Temperature | <= -75.0 °C | <= -103 °F | ASTM D746 |
| Optical Properties | Metric | English | Comments |
| Haze | 7.5 % | 7.5 % | ISO 14782 |
| Gloss | 72 % | 72 % | 45°; ASTM D2457 |