- 熔体流动速率 [g/10min]: 12.0
- 密度 [g/cm3]: 0.92
- 拉伸强度 [MPa]: 10.3
- 弯曲模量 [MPa]: 0.121
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ASTM D792 |
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 190 °C | 12 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 43 | 43 | ASTM D2240 |
| Tensile Strength, Yield | 10.3 MPa | 1500 psi | ASTM D638 |
| Elongation at Break | 400 % | 400 % | ASTM D638 |
| Flexural Modulus | 0.121 GPa | 17.5 ksi | 1% Secant; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 85.0 °C | 185 °F | Rate A, Loading 1 (10 N); ASTM D1525 |