- 熔体流动速率 [g/10min]: 70.0
- 密度 [g/cm3]: 0.912
- 弯曲模量 [MPa]: 0.121
- 脆化温度 [℃]: -10.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.912 g/cc | 0.0329 lb/in³ | ASTM D1505 |
| Particle Mesh Size | 50 Mesh | 50 Mesh | Irregular shape. ETM = Equistar Test Method; ETM Malvern |
| Melt Flow | 70 g/10 min | 70 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 51 | 51 | ASTM D2240 |
| Tensile Strength at Break | 6.89 MPa | 1000 psi | ASTM D638 |
| Elongation at Break | 200 % | 200 % | ASTM D638 |
| Flexural Modulus | 0.121 GPa | 17.5 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 102 °C | 216 °F | ASTM D3418 |
| Vicat Softening Point | 78.0 °C | 172 °F | ASTM D1525 |
| Brittleness Temperature | -10.0 °C | 14.0 °F | ASTM D746 |