- 熔体流动速率 [g/10min]: 6.5
- 密度 [g/cm3]: 0.92
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ASTM D1505 | ||
| Thickness | 31.8 microns | 1.25 mil | 2.2:1 BUR | ||
| Melt Flow | 6.5 g/10 min | 6.5 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 225 % | 225 % | ASTM D882 | ||
| Film Elongation at Break, TD | 450 % | 450 % | ASTM D882 | ||
| Elmendorf Tear Strength MD | 350 g | 350 g | ASTM D1922 | ||
| Elmendorf Tear Strength TD | 150 g | 150 g | ASTM D1922 | ||
| Dart drop Test | 90.0 g | 0.198 lb | F50; ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 17.2 MPa | 2500 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 13.9 MPa | 2020 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 146 MPa | 21200 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 165 MPa | 24000 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Vicat Softening Point | 85.0 °C | 185 °F | ASTM D1525 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 8.0 % | 8.0 % | ASTM D1003 | ||
| Gloss | 62 % | 62 % | at 45°; ASTM D2457 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 163 °C | 325 °F | |||
| Descriptive Properties | |||||
| Antiblock | High | ||||
| Slip | High | ||||