- 熔体流动速率 [g/10min]: 7.5
- 密度 [g/cm3]: 0.924
- 拉伸强度 [MPa]: 13.6
- 弯曲模量 [MPa]: 0.340
- 脆化温度 [℃]: -42.8
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in³ | ASTM D1505 |
| Melt Flow | 7.50 g/10 min | 7.50 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 48.0 | 48.0 | ASTM D2240 |
| Tensile Strength, Yield | 13.6 MPa | 1970 psi | ASTM D638 |
| Elongation at Yield | 13.0 % | 13.0 % | ASTM D638 |
| Flexural Modulus | 0.340 GPa | 49.3 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -42.8 °C | -45.0 °F | F50; ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 163 °C | 325 °F | |
| Middle Barrel Temperature | 177 °C | 350 °F | |
| Front Barrel Temperature | 177 °C | 350 °F | |
| Nozzle Temperature | 177 °C | 350 °F | |
| Compliance Properties | Metric | English | Comments |
| FDA | Yes | Yes | |