- 熔体流动速率 [g/10min]: 6.8
- 密度 [g/cm3]: 0.921
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in³ | ExxonMobil Method | ||
| Melt Flow | 6.8 g/10 min | 6.8 g/10 min | ExxonMobil Method | ||
| Antiblock Level | 24000 ppm | 24000 ppm | |||
| Slip Level | 1350 ppm | 1350 ppm | |||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 8.96 MPa | 1300 psi | at 2% offset; ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 9.65 MPa | 1400 psi | at 2% offset; ASTM D882 | ||
| Film Elongation at Break, MD | 380 % | 380 % | ASTM D882 | ||
| Film Elongation at Break, TD | 610 % | 610 % | ASTM D882 | ||
| Film Elongation at Yield, MD | 7.0 % | 7.0 % | ASTM D882 | ||
| Film Elongation at Yield, TD | 7.4 % | 7.4 % | ASTM D882 | ||
| Elmendorf Tear Strength, MD | 5.12 g/micron | 130 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 3.31 g/micron | 84.0 g/mil | ASTM D1922 | ||
| Dart Drop | 2.60 g/micron | 66.0 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 20.0 MPa | 2900 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 20.7 MPa | 3000 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 157 MPa | 22800 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 182 MPa | 26400 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 110 °C | 230 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Vicat Softening Point | 87.2 - 91.1 °C | 189 - 196 °F | ASTM D1525 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 4.0 % | 4.0 % | ASTM D1003 | ||
| Gloss | 83 % | 83 % | 45°; ASTM D2457 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.