- 熔体流动速率 [g/10min]: 2.4
- 密度 [g/cm3]: 0.923
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.923 g/cc | 0.0333 lb/in³ | ExxonMobil Method |
| Thickness | 38.1 microns | 1.50 mil | |
| Melt Flow | 2.4 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.4 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 11.0 MPa | 1600 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 11.7 MPa | 1700 psi | ASTM D882 |
| Film Elongation at Break, MD | 270 % | 270 % | ASTM D882 |
| Film Elongation at Break, TD | 660 % | 660 % | ASTM D882 |
| Puncture Energy | 2.03 J | 1.50 ft-lb | ExxonMobil Method |
| Elmendorf Tear Strength MD | 480 g | 480 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 120 g | 120 g | ASTM D1922 |
| Dart drop Test | 100 g | 0.221 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 28.6 MPa | 4150 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 24.0 MPa | 3480 psi | ASTM D882 |
| 1% Secant Modulus, MD | 220 MPa | 31900 psi | ASTM D882 |
| 1% Secant Modulus, TD | 269 MPa | 39000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 112 °C | 233 °F | Peak Melting Temperature; ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
| Haze | 5.3 % | 5.3 % | ASTM D1003 |
| Gloss | 72 % | 72 % | 45°; ASTM D2457 |
| Transmission, Visible | 90.0 % | 90.0 % | clear; thickness not quantified |