- 密度 [g/cm3]: 0.924
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in³ | ASTM D1505 | ||
| Particle Size | >= 150 µm | >= 150 µm | pan, 13% | ||
| <= 800 µm | <= 800 µm | sieve < 5% | |||
| Melt Index of Compound | 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 6.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 50 | 50 | ASTM D2240 | ||
| Elongation at Break | 100 % | 100 % | 50 mm/min; ASTM D638 | ||
| Tensile Modulus | 0.200 GPa | 29.0 ksi | 1 mm/min; ASTM D638 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 111 °C | 232 °F | DSC; ASTM D3418 | ||
| Vicat Softening Point | 82.0 °C | 180 °F | ASTM D1525 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 200 °C | 392 °F | recommended | ||
| Descriptive Properties | |||||
| Max Dry Flow | max 31 sec/100g | ASTM | |||