- 熔体流动速率 [g/10min]: 0.3
- 密度 [g/cm3]: 0.921
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in³ | ISO 1183 |
| Melt Flow | 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.30 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Stress | 11.0 MPa | 1600 psi | at Yield, TD; ISO 527 |
| 11.0 MPa | 1600 psi | at Yield, MD; ISO 527 | |
| Elongation at Break | 200 % | 200 % | ISO 527, MD |
| 500 % | 500 % | ISO 527, TD | |
| Modulus of Elasticity | 0.190 GPa | 27.6 ksi | TD; ISO 527 |
| 0.190 GPa | 27.6 ksi | MD; ISO 527 | |
| Tensile Impact | 300 J/cm | 562 ft-lb/in | ASTM D4272 |
| Coefficient of Friction | 1.0 | 1.0 | ASTM D1894 |
| Tear Strength | 30.0 kN/m | 171 pli | TD; ISO 6383-2 |
| 30.0 kN/m | 171 pli | MD; ISO 6383-2 | |
| Optical Properties | Metric | English | Comments |
| Haze | 14 % | 14 % | ASTM D1003A |
| Gloss | 45 % | 45 % | ASTM D2457 |