- 熔体流动速率 [g/10min]: 0.8
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 0.921 g/cc | 0.921 g/cc | ASTM D1505 | ||
| Water Vapor Transmission | 12.0 g/m²/day | 0.773 g/100 in²/day | |||
| Oxygen Transmission Rate | 2000 cc/m²/day | 129 cc/100 in²/day | |||
| Nitrogen Transmission | 3500 cc-mm/m²-24hr-atm | 8890 cc-mil/100 in²-24hr-atm | |||
| Melt Flow | 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.80 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 550 % | 550 % | ASTM D882 | ||
| Film Elongation at Break, TD | 650 % | 650 % | ASTM D882 | ||
| Elmendorf Tear Strength MD | 280 g | 280 g | ASTM D1922 | ||
| Elmendorf Tear Strength TD | 350 g | 350 g | ASTM D1922 | ||
| Dart drop Test | 230 g | 0.507 lb | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 21.7 MPa | 3150 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 20.7 MPa | 3000 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 110 °C | 230 °F | DSC | ||
| Vicat Softening Point | 94.0 °C | 201 °F | ASTM D1525 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 8.0 % | 8.0 % | ASTM D1003 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 170 - 200 °C | 338 - 392 °F | |||
| Blow-up Ratio (BUR) | 1.5 - 2.0 | 1.5 - 2.0 | |||
| Descriptive Properties | |||||
| Slip Coefficient | 0.15 | ASMT D1894 | |||