- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 1.02
- 缺口冲击强度: 4.97
- 拉伸强度 [MPa]: 16.5
- 弯曲模量 [MPa]: 0.214
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in³ | ASTM D792 |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 16.5 MPa | 2400 psi | ASTM D638 |
| Elongation at Break | 900 % | 900 % | ASTM D638 |
| Flexural Modulus | 0.214 GPa | 31.0 ksi | ASTM D790 |
| Izod Impact, Notched | 4.97 J/cm | 9.30 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Flammability, UL94 | V-2 | V-2 | 0.125 in |
| V-2 | V-2 | 0.0625 in | |